Butt Joining of Aluminum Sheets Using Face Filler Friction Stir Spot Welding
DOI:
https://doi.org/10.31181/rme448Keywords:
Butt Joining, Friction, Manufacturing Process, Aluminum Alloy, Face FillerAbstract
Friction stir spot welding FSSW, as a general rule, is adopted and limited for joining sheets of similar or dissimilar metals in a lap joint configuration, and it cannot be used in butt jointsss. The idea of this study is to weld two AA 1050 aluminum sheets in a butt joint configuration, having a thickness of 2 mm each, by using a face filler disk from the same AA 1050 alloy of 1 mm thickness via friction stir spot welding. A stir tool (rod or welding tool) is made from HSS high-speed steel. A special fixture is manufactured to hold and weld the sheets with the facial filling in a butt configuration. Three different rotational speeds (1120, 1400, and 1800 revolutions per minute) with a linear movement in a direction perpendicular to the facial filling and then to the sheets were used. The samples were welded with and without preheating, with the stirring tool lowered by 1 mm in a vertical orientation. The best result obtained regarding the force applied to break the welded sample is 4000 Newtons as a tensile force, with a joint efficiency of 72% compared to the strength of the original metal. Also, we obtained a tensile strength to break the welded joint of 125 MPa compared to the tensile strength of the original metal, with a joint efficiency of 113% of the tensile strength of the original metal. The cross-sectional area of the fracture was also observed, which was acceptable from the point of view of microscopic examination. No traces of the contact area between the two sheets were seen, and the fusion of the two sheets was perfect. With the elimination of the keyhole, considered a flaw in the standard friction stir spot welding procedure, it was possible to obtain keyhole-less areas while maintaining adequate joint strength. The metallurgical bonding between the face filler disc and the lower sheet causes the disc to become a part of the spot when inserted into the lower sheet.
References
Abdullah, I., Mejbel, M., & Al-bhadle, B. (2024). Double stage friction stir spot extrusion welding: a novel manufacturing technique for joining sheets. Experimental Techniques, 48(2), 323-342. https://doi.org/10.1007/s40799-023-00660-2
Abdullah, I., Ridha, M., Barrak, O., Hussein, S., & Hussein, A. (2021). Joining of Aa1050 sheets via two stages of friction spot technique. Journal of Mechanical Engineering Research and Developments, 44(4), 305-317. https://www.researchgate.net/profile/Osamah-Barrak/publication/351069050_Joining_of_Aa1050_Sheets_Via_Two_Stages_of_Friction_Spot_Technique/links/6082c827907dcf667bba2119/Joining-of-Aa1050-Sheets-Via-Two-Stages-of-Friction-Spot-Technique.pdf
Abdullah, I. T., & Hussein, S. K. (2018). Improving the joint strength of the friction stir spot welding of carbon steel and copper using the design of experiments method. Multidiscipline Modeling in Materials and Structures, 14(5), 908-922. https://doi.org/10.1108/MMMS-02-2018-0025
Abdullah, I. T., & Hussein, S. K. (2019). Shear strength and temperature distribution model of friction spot lap joint of high density polyethylene with aluminum alloy 7075. International Journal of Structural Integrity, 10(4), 469-483. https://doi.org/10.1108/IJSI-05-2018-0025
Abdullah, I. T., Hussein, S. K., & Hussein, A. K. (2020a). Joining of AA6061 to polyvinyl chloride via hot extrusion. International Journal of Structural Integrity, 11(2), 286-302. https://doi.org/10.1108/IJSI-08-2019-0081
Abdullah, I. T., Hussein, S. K., & Hussein, A. K. (2020b). Joining aluminium alloy to pre-holed carbon steel using the aluminium extrusion method with friction spot welding. International Journal of Structural Integrity, 11(6), 849-860. https://doi.org/10.1108/IJSI-10-2019-0112
Abdullah, I. T., Mejbel, M. K., & Al-Filfily, A. A. (2025). Joining 1.1‐and 2.1‐mm Al Sheets by Friction Stir Spot Welding. Material Design & Processing Communications, 2025(1), 3110429. https://doi.org/10.1155/mdp2/3110429
Akinlabi, E. T., Sanusi, K. O., Muzenda, E., & Akinlabi, S. A. (2017). Material behaviour characterization of friction stir spot welding of copper. Materials Today: Proceedings, 4(2), 166-177. https://doi.org/10.1016/j.matpr.2017.01.010
Ali, K. G., Muhmmed, A. A., Taieh, N. K., & Mejbel, M. K. (2022). Tribological and mechanical performance of epoxy reinforced by fish scales powder. Revue Des Composites et Des Matériaux Avancés, 32(3), 149. https://doi.org/10.18280/rcma.320306
Alizadeh-Sh, M., Fæster, S., Farahani, E., Sarhadi, A., Tiedje, N., Eder, M., & Danielsen, H. (2024). Microstructural evolution during welding of high Si solution-strengthened ferritic ductile cast iron using different filler metals. Metallurgical and Materials Transactions A, 55(7), 2309-2323. https://doi.org/10.1007/s11661-024-07399-4.
Aydin, H., Tuncel, O., Umur, Y., Tutar, M., & Bayram, A. (2017). Effect of welding parameters on microstructure and mechanical properties of aluminum alloy AA6082-T6 friction stir spot welds. Indian J. Eng. Mater. Sci, 24(3), 215-227. https://avesis.uludag.edu.tr/yayin/4ea382f2-2dd3-4008-81c2-ef4f09b56d33/effect-of-welding-parameters-on-microstructure-and-mechanical-properties-of-aluminum-alloy-aa6082-t6-friction-stir-spot-welds
Baudin, T., Bozzi, S., Brisset, F., & Azzeddine, H. (2023). Local microstructure and texture development during friction stir spot of 5182 aluminum alloy. Crystals, 13(3), 540. https://doi.org/10.3390/cryst13030540
Beddai, A. A., Badday, B. A., Al-Yaqoobi, A. M., Mejbel, M. K., Al Hachim, Z. S., & Mohammed, M. K. (2022). Color removal of textile wastewater using electrochemical batch recirculation tubular upflow cell. International Journal of Chemical Engineering, 2022(1), 4713399. https://doi.org/10.1155/2022/4713399
Bergmann, J. P., Petzoldt, F., Schürer, R., & Schneider, S. (2013). Solid-state welding of aluminum to copper—case studies. Welding in the World, 57(4), 541-550. https://doi.org/10.1007/s40194-013-0049-z
Chen, B.-Q., Liu, K., & Xu, S. (2024). Recent advances in aluminum welding for marine structures. Journal of Marine Science and Engineering, 12(9), 1539. https://doi.org/10.3390/jmse12091539
Chen, K., Liu, X., & Ni, J. (2017). Keyhole refilled friction stir spot welding of aluminum alloy to advanced high strength steel. Journal of Materials Processing Technology, 249, 452-462. https://doi.org/10.1016/j.jmatprotec.2017.06.039
Dong, H., Chen, S., Song, Y., Guo, X., Zhang, X., & Sun, Z. (2016). Refilled friction stir spot welding of aluminum alloy to galvanized steel sheets. Materials & Design, 94, 457-466. https://doi.org/10.1016/j.matdes.2016.01.066
Fan, W., Chu, Q., Yang, X., Li, W., Zou, Y., & Hao, S. (2023). Microstructure and mechanical properties of probeless friction stir spot welded AlLi alloy joints via fast electric pulse treatment: A comparative study. Materials Characterization, 205, 113276. https://doi.org/10.1016/j.matchar.2023.113276
Heidarzadeh, A., Mironov, S., Kaibyshev, R., Çam, G., Simar, A., Gerlich, A., Khodabakhshi, F., Mostafaei, A., Field, D. P., & Robson, J. D. (2021). Friction stir welding/processing of metals and alloys: A comprehensive review on microstructural evolution. Progress in Materials Science, 117, 100752. https://doi.org/10.1016/j.pmatsci.2020.100752
Huang, S., Wang, Y., Fan, M., Huo, X., Ma, N., & Lu, F. (2023). The heterogeneous microstructure of laser welded joint and its effect on mechanical properties for dissimilar 9Cr steel and alloy 617. Journal of Materials Research and Technology, 26, 1094-1106. https://doi.org/10.1016/j.jmrt.2023.07.281
Hussein, S. K., Abdullah, I. T., & Hussein, A. K. (2019). Spot lap joining of AA5052 to AISI 1006 by aluminium extrusion via friction forming technique. Multidiscipline Modeling in Materials and Structures, 15(6), 1337-1351. https://doi.org/10.1108/MMMS-04-2019-0082
Ikumapayi, O. M., & Akinlabi, E. T. (2019). Recent advances in keyhole defects repairs via refilling friction stir spot welding. Materials Today: Proceedings, 18, 2201-2208. https://doi.org/10.1016/j.matpr.2019.06.663
Kesharwani, R., Jha, K. K., Imam, M., Sarkar, C., & Barsoum, I. (2024). Correlation of microstructure, texture, and mechanical properties of friction stir welded Joints of AA7075-T6 plates using a flat tool pin profile. Heliyon, 10(3). https://doi.org/10.1016/j.heliyon.2024.e25449
Kubit, A., Derazkola, H. A., Jurczak, W., Ochałek, K., Myśliwiec, P., Macek, W., Łastowska, O., Podulka, P., & Slota, J. (2025). Effects of process parameters on dynamic and static load capacity of EN AW-2024-T3 aluminum alloy joints prepared by friction stir welding. Archives of Civil and Mechanical Engineering, 25(3), 153. https://doi.org/10.1007/s43452-025-01204-8
Luo, C., Li, X., Song, D., Zhou, N., Li, Y., & Qi, W. (2016). Microstructure evolution and mechanical properties of friction stir welded dissimilar joints of Mg–Zn–Gd and Mg–Al–Zn alloys. Materials Science and Engineering: A, 664, 103-113. https://doi.org/10.1016/j.msea.2016.03.117
Mejbel, A., Khalaf, M. M., & Kwad, A. M. (2021). Improving the machined surface of AISI H11 tool steel in milling process. J. Mech. Eng. Res. Dev, 44(4), 58-68. https://www.researchgate.net/profile/Mohanad-Mejbel/publication/351117059_Improving_the_Machined_Surface_of_AISI_H11_Tool_Steel_in_Milling_Process/links/608856ff907dcf667bcabfec/Improving-the-Machined-Surface-of-AISI-H11-Tool-Steel-in-Milling-Process.pdf
Mejbel, M. K., & Abdullah, I. T. (2025). Friction Stir Spot Extrusion Joining With Its Metal Flow Investigation. Advances in Materials Science and Engineering, 2025(1), 1617392. https://doi.org/10.1155/amse/1617392
Mejbel, M. K., Abdullah, I. T., & Taieh, N. K. (2022). Thin wall manufacturing improvement using novel simultaneous double-sided cutter milling technique. International Journal of Automotive and Mechanical Engineering, 19(1), 9519-9529. https://doi.org/10.15282/ijame.19.1.2022.15.0734
Mejbel, M. K., Hussein, S. K., & Abdullah, I. T. (2025). Friction stir consolidation for recycling AA6061 chips with its metal flow investigation for billet production. Journal of Engineering Research, 13(2), 1170-1183. https://doi.org/10.1016/j.jer.2024.04.010
Mohammad, S., Daway, E., & Mejbel, M. (2022). Friction Stir Spot Joining of Aa6061-T6 To Fiber Glass Composite Material. Int J Tech Phys Probl Eng, 14(4), 203-210. https://www.researchgate.net/profile/Mohanad-Mejbel/publication/366682745_FRICTION_STIR_SPOT_JOINING_OF_AA6061-T6_TO_FIBER_GLASS_COMPOSITE_MATERIAL/links/63ae35b5a03100368a3b3cdc/FRICTION-STIR-SPOT-JOINING-OF-AA6061-T6-TO-FIBER-GLASS-COMPOSITE-MATERIAL.pdf
Muhayat, N., Larasati, R. D., Putri, E. D., & Budiana, E. P. (2025). Effect of tool diameter on the joint properties of AA6061 hollow panels using a novel one-step double-acting Friction Stir Weld method. Journal of Advanced Joining Processes, 11, 100277. https://doi.org/10.1016/j.jajp.2024.100277
Ojo, O. O., Taban, E., & Kaluc, E. (2015). Friction stir spot welding of aluminum alloys: a recent review. Materials Testing, 57(7-8), 609-627. https://doi.org/10.3139/120.110752
Oudah, M. H., Mejbel, M. K., & Allawi, M. K. (2021). R134a flow boiling heat transfer (FBHT) characteristics in a refrigeration system. J. Mech. Eng. Res. Dev, 44(4), 69-83. https://www.researchgate.net/profile/Mohanad-Mejbel/publication/350107942_R134a_Flow_Boiling_Heat_Transfer_FBHT_Characteristics_in_a_Refrigeration_System/links/6051d29da6fdccbfeae674ae/R134a-Flow-Boiling-Heat-Transfer-FBHT-Characteristics-in-a-Refrigeration-System.pdf
Paidar, M., Bokov, D., Mehrez, S., Nasution, M. K., Ojo, O. O., & Zain, A. M. (2022). The influence of the backing plate materials on microstructure and mechanical properties of friction spot extrusion brazing of AA2024-T3 aluminum alloy and Brass sheets. Journal of Manufacturing Processes, 74, 28-39. https://doi.org/10.1016/j.jmapro.2021.12.002
Popović, O., Prokić-Cvetković, R., Burzić, M., Lukić, U., & Beljić, B. (2014). Fume and gas emission during arc welding: Hazards and recommendation. Renewable and sustainable energy reviews, 37, 509-516. https://doi.org/10.1016/j.rser.2014.05.076
Prihajatno, M., Ilman, M., Sriwijaya, R., Muslih, M., & Apriansyah, R. (2024). Tensile and fatigue properties of friction stir AZ31B-H24 magnesium alloy welded joints under the influences of pin geometry and tool rotation rate. Journal of Advanced Joining Processes, 9, 100202. https://doi.org/10.1016/j.jajp.2024.100202
Rao, H., Jordon, J., Boorgu, S., Kang, H., Yuan, W., & Su, X. (2017). Influence of the key-hole on fatigue life in friction stir linear welded aluminum to magnesium. International Journal of Fatigue, 105, 16-26. https://doi.org/10.1016/j.ijfatigue.2017.08.012
Reimann, M., Goebel, J., & dos Santos, J. F. (2017). Microstructure and mechanical properties of keyhole repair welds in AA 7075-T651 using refill friction stir spot welding. Materials & Design, 132, 283-294. https://doi.org/10.1016/j.matdes.2017.07.013
Rishad, S. M. A., Islam, M. A., & Islam, M. S. (2025). Analysis of stress distribution of CFRP bonded joints: A study of numerical and machine learning approach. Heliyon, 11(3). https://doi.org/10.1016/j.heliyon.2025.e42440
Rosendo, T., Parra, B., Tier, M., Da Silva, A., Dos Santos, J., Strohaecker, T., & Alcântara, N. (2011). Mechanical and microstructural investigation of friction spot welded AA6181-T4 aluminium alloy. Materials & Design, 32(3), 1094-1100. https://doi.org/10.1016/j.matdes.2010.11.017
Sato, Y. S., Park, S. H. C., & Kokawa, H. (2001). Microstructural factors governing hardness in friction-stir welds of solid-solution-hardened Al alloys. Metallurgical and Materials Transactions A, 32(12), 3033-3042. https://doi.org/10.1007/s11661-001-0178-7
Shi, Y., Yue, Y., Zhang, L., Ji, S., & Wang, Y. (2018). Refill friction stir spot welding of 2198-T8 aluminum alloy. Transactions of the Indian Institute of Metals, 71(1), 139-145. https://doi.org/10.1007/s12666-017-1146-2
Tao, W., Yong, Z., Xuemei, L., & Matsuda, K. (2016). Special grain boundaries in the nugget zone of friction stir welded AA6061-T6 under various welding parameters. Materials Science and Engineering: A, 671, 7-16. https://doi.org/10.1016/j.msea.2016.06.050
Tunçel, O., Tutar, M., & Bayram, A. (2020). Effect of tool pin profile on the hook geometry and mechanical properties of a friction stir spot welded AA6082-T6 aluminum alloy. Transactions of the Canadian Society for Mechanical Engineering, 45(2), 233-248. https://doi.org/10.1139/tcsme-2020-0035
Uematsu, Y., Tokaji, K., Tozaki, Y., Kurita, T., & Murata, S. (2008). Effect of re-filling probe hole on tensile failure and fatigue behaviour of friction stir spot welded joints in Al–Mg–Si alloy. International Journal of Fatigue, 30(10-11), 1956-1966. https://doi.org/10.1016/j.ijfatigue.2008.01.006.
Van, D., Lee, S. H., Kim, K., & Sim, H. (2019). Weldability and lamellar tearing susceptibility of high-strength SN 490C steel plates. Metals, 9(5), 551. https://doi.org/10.3390/met9050551
Wang, S., Zhang, Y., Wen, G., Qi, J., Zhai, W., & Gao, W. (2024). Compressive behavior and deformation mechanisms of gradient microstructures in a dissimilar welded joint. Physica Scripta, 99(9), 095960. https://doi.org/10.1088/1402-4896/ad6d19
Xu, W., Wang, H., Lu, H., Liu, Y., & Dong, J. (2021). Effect of thermal exposure on microstructure and mechanical properties of friction stir welding 7B50-T7451 aluminium alloy thick plate joint. Journal of Materials Research and Technology, 15, 6415-6433. https://doi.org/10.1016/j.jmrt.2021.11.082
Yu, M., Zhao, H., Zhang, Z., Zhou, L., & Song, X. (2022). Friction surfacing assisted refilled friction stir spot welding of AA6061 alloy and Q235 steel. Journal of Manufacturing Processes, 77, 1-12. https://doi.org/10.1016/j.jmapro.2022.03.006
Zhang, Z.-k., & Gang, Z. (2014). Friction stir keyholeless spot welding of AZ31 Mg alloy-mild steel. Transactions of Nonferrous Metals Society of China, 24(6), 1709-1716. https://doi.org/10.1016/S1003-6326(14)63244-1
Downloads
Published
Issue
Section
License
Copyright (c) 2025 Reports in Mechanical Engineering
This work is licensed under a Creative Commons Attribution 4.0 International License.